The results of nanostructured PACVD coating to prevent biofouling are presented
COBISS.SI-ID: 707754
Recrystallization of amorphous powder was studied using multi-technique approach based on electron beams, It has been found that annealing of the amorphous Fe-Si-B powder at a temperature of 500 degrees C leads to the formation of alpha-Fe phase in the form of two, three and four-branch dendritic grains. The Fe2B boride is crystallised at temperatures of over 500 degrees C.
COBISS.SI-ID: 671658
The passive films established on the two stainless steels in the borate buffer solution at pH = 9.3 contained the oxides of two main elements, i.e., Fe and Cr. The oxides of the alloying elements Ni and, optionally, Mo, also contribute to the passive layer.
COBISS.SI-ID: 707498
The cold-rolled samples of Fe-Si-Al alloys were annealed in the temperature range 320-1 120 K in the ultra-high-vacuum chamber of a field-emission Auger electron spectrometer, and subsequently characterized by Auger electron spectroscopy (AES). The Cu segregation rate was estimated based on the surface concentration of Cu after annealing at a given temperature.
COBISS.SI-ID: 578218
Wear and plastic deformation the performance od high-speed steels in several applications is not adequate and should be further improved. In recent years there has been an increased utilization of higher strength steels.
COBISS.SI-ID: 8999195